Yu Cheng, Yin Deng Feng and Yu Xin Xiang
The mechanical properties and microstructures of Al-Li-Cu-Mg-Ag alloy after different solution treatments were investigated by means of Optical Microscopy (OM), tensile test, hardness and electrical conductivity tests, Differential Scanning Calorimetry (DSC), Energy Dispersive X-ray (EDX), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). Results show that the tensile strength and hardness increase firstly and then decrease with elevating solution temperature when the holding time is kept for 30 min, and the maximum strength and hardness are reached when temperature is 520°C. The mechanical properties of alloy also display similar trend, which increase firstly and then decrease with increasing solution time when alloy is treated at 520°C. The tensile strength, hardness and elongation of the alloy solution treated at 520°C/30 min are 566 Mpa(σb),512 Mpa(σ0.2), 148HB and 8.23% (δ), respectively. TEM shows that an amount of T1 (Al2CuLi) phases are finely and dispersedly distributed in Al substrates, which can be an explanation of a mixed fracture mode of transgranular and intergranular delamination cracks observed by SEM.
分享此文章
English 
Spanish 
Russian 
German 
French 
Japanese 
Portuguese 
Hindi 