The Aging Degree Analysis of EPR Cable Insulation Based on Hardness Retention Rate Measurement

Abstract

Meng Xiao-Kai, Han Pei-Jie, Liu Xinyuan and Jin Tao

Based on the accelerated thermal aging analysis of Ethylene-Propylene Rubber (EPR) cables, the theoretical relationship between elongation at break retention rate (EAB%) and hardness retention rate was deduced from the mathematical principles of hardness test. The relation curve was compared with the measurement values, and the result shows that there is high coincidence degree between theoretical curve and measurement values. After researching on the experimental data of EAB% and hardness retention rate, combining the “time-temperature shift factors” with Arrhenius equation, the lifetime termination index on account of hardness retention rate is analyzed when the EAB% reduced to 30%-50%. According to comparing theoretical values with the experimental results, hardness retention rate decreased to 10% was proposed as the lifetime termination index of EPR cable.

免责声明: 此摘要通过人工智能工具翻译,尚未经过审核或验证

分享此文章

索引于

相关链接

arrow_upward arrow_upward